POM is a high-performance engineering plastic with similar hardness, strength, and steel properties to metals. It has excellent self-lubrication and chemical resistance over a wide range of temperature and humidity. POM, with a lower cost than many other engineering plastics, is replacing some markets traditionally occupied by metals, such as replacing zinc, brass, aluminum, and steel to make many components, and is widely used in fields such as electronics and electronics, machinery, automobiles, building materials, agriculture, and healthcare.
| Product information |
| Color | All Color |
| Material Shape | Pellets |
| Polymer | Copolymer |
| Dielectric | Strength | IEC 60243 | 26 | KV/mm |
| Surface | Resistivity | IEC 60093 | 3E+16 | |
| Volume | Resistivity | IEC 60093 | 8E+14 | Ω.cm |
| Flame | Rating All Color 0.71mm | UL94 | HB | |
| Flame | Rating All Color 1.5mm | UL94 | HB | |
| Flame | Rating All Color 3.0mm | UL94 | HB | |
| Flame | Rating All Color 6.0mm | UL94 | HB | |
| Charpy | Notch Impact 23°C | ISO 179 | 6 | kJ/m² |
| Charpy | Notch Impact -30°C | ISO 179 | 6 | kJ/m² |
| Charpy | Un-notch Impact 23°C | ISO 179 | 190 | kJ/m² |
| Charpy | Un-notch Impact -30°C | ISO 179 | 180 | kJ/m² |
| Elongation | 23°C | ISO 527 | 10 | % |
| Flexural | Modulus 23°C | ISO 178 | 2550 | MPa |
| Izod | Notch Impact 23°C | ISO 180 | 5.7 | kJ/m² |
| Tensile | Modulus 23°C | ISO 527 | 2760 | MPa |
| Tensile | Strength 23°C | ISO 527 | 66 | MPa |
| Tensile | Creep Modulus 1hr | ISO 899 | 2450 | MPa |
| Tensile | Creep Modulus 1000hr | ISO 899 | 1350 | MPa |
| Density | | ISO 1183 | 1.41 | g/cm³ |
| Melt | Index 190°C 2.16kg | ISO 1133 | 8 | cm³/10min |
| Shrinkage | Flow | ISO 294 | 2 | % |
| Shrinkage | xFlow | ISO 294 | 1.9 | % |
| Water | Absorption 23°C 24hr | ISO 62 | 0.75 | % |
| Water | Absorption 23°C 50RH | ISO 62 | 0.2 | % |
| CLE | Flow | ISO 11359 | 1.2E-4 | cm/cm/°C |
| CLE | xFlow | ISO 11359 | 1.2E-4 | cm/cm/°C |
| HDT | Unannealed 0.45MPa | ISO 75 | 158 | °C |
| HDT | Unannealed 1.8MPa | ISO 75 | 101 | °C |
| Melting | Temperature | ISO 11357 | 165 | °C |
| | | | | | | |