HOMEPRODUCTSPOMPOM M90-45 Injection grade Good weather resistance plastic raw materials

PRODUCTS

  • POM M90-45 Injection grade Good weather resistance plastic raw materials
  • POM M90-45 Injection grade Good weather resistance plastic raw materials
  • POM M90-45 Injection grade Good weather resistance plastic raw materials
  • POM M90-45 Injection grade Good weather resistance plastic raw materials
  • POM M90-45 Injection grade Good weather resistance plastic raw materials

POM M90-45 Injection grade Good weather resistance plastic raw materials

POM is a high-performance engineering plastic with similar hardness, strength, and steel properties to metals. It has excellent self-lubrication and chemical resistance over a wide range of tempera...

Free to contact us

  • Product Struction

POM is a high-performance engineering plastic with similar hardness, strength, and steel properties to metals. It has excellent self-lubrication and chemical resistance over a wide range of temperature and humidity. POM, with a lower cost than many other engineering plastics, is replacing some markets traditionally occupied by metals, such as replacing zinc, brass, aluminum, and steel to make many components, and is widely used in fields such as electronics and electronics, machinery, automobiles, building materials, agriculture, and healthcare.

 

Product information
Color NC
Material Shape Pellets
Process Injection molding
Polymer Copolymer
Viscosity Medium viscosity
Features Good weather resistance
Application Automotive partsBike partsFastenersOutdoor Cactivities ApplicationsToys partsConstruction ApplicationsSafety helmetWindows & DoorsGearsIndustrial ApplicationsMachinery partsPipe fittingPower toolsMotorcycle partsOutdoor electrical
Additives Lubricant Mold Releases UV Stabilizer
Electrical properties Condition Standard Value Unit
Dielectric Strength   3.0mm IEC 60243 19 KV/mm
Surface Resistivity IEC 60093 4E+15 Ω
Volume Resistivity IEC 60093 4E+14 Ω.cm
Flammability Condition Standard Value Unit
Flame Rating   All Color 0.75mm UL94 HB
Hardness Condition Standard Value Unit
Rockwell Hardness   M(Scale) ISO 2039 80
Mechanical behavior Condition Standard Value Unit
Charpy Notch Impact   23°C ISO 179 6.0 kJ/m²
Elongation Break ISO 527 35 %
Flexural Strength ISO 178 87 MPa
Flexural Modulus ISO 178 2500 MPa
Friction Coefficient   Dynamic VS C-Steel 0.49MPa 0.3m/s thrust JIS K7218 0.45
Friction Coefficient   Dynamic VS M90-44 0.06MPa 0.15m/s thrust JIS K7218 0.37
Specific Wear Rate   VS C-Steel 0.3m/s 0.49MPa Material Side thrust JIS K7218 0.001 mm³/(N・km)
Specific Wear Rate   VS C-Steel 0.3m/s 0.49MPa Steel Side thrust JIS K7218 0.00001 mm³/(N・km)
Tensile Modulus ISO 527 2700 MPa
Tensile Strength ISO 527 62 MPa
Physical property Condition Standard Value Unit
Density ISO 1183 1.41 g/cm³
Melt Index   190°C 2.16kg ISO 1133 9 g/10min
Melt Index   190°C 2.16kg ISO 1133 8 cm³/10min
Shrinkage Flow 60x60x2mm ISO 294 2.0 %
Shrinkage xFlow 60x60x2mm ISO 294 2.0 %
Water Absorption   23°C 24hr 1.00mm ISO 62 0.6 %
Thermal Condition Standard Value Unit
CLE Flow 23~55°C INTERNAL METHOD 1.2E-4 cm/cm/°C
CLE xFlow 23~55°C INTERNAL METHOD 1.2E-4 cm/cm/°C
HDT 1.8MPa ISO 75 95 °C