LUCEL POM FW-715C Injection grade Switch application raw material

Polyoxymethylene (POM), also known as polyacetal or acetal, is a high-density, high-crystallinity thermoplastic engineering plastic, commonly referred to as Delrin or engineering plastic steel. It is polymerized from formaldehyde and mainly divided into POM homopolymer (POM-H) and POM copolymer (POM-K). This material is widely used in various engineering applications due to its excellent physical, mechanical, and chemical properties, especially its friction resistance.

ree to contact us

  • Product Struction

Polyoxymethylene (POM), also known as polyacetal or acetal, is a high-density, high-crystallinity thermoplastic engineering plastic, commonly referred to as Delrin or engineering plastic steel. It is polymerized from formaldehyde and mainly divided into POM homopolymer (POM-H) and POM copolymer (POM-K). This material is widely used in various engineering applications due to its excellent physical, mechanical, and chemical properties, especially its friction resistance.

POM materials have high-density crystallinity without side chains, exhibiting superior comprehensive performance. It is a smooth, glossy, hard, and dense material, typically pale yellow or white, capable of long-term use in the temperature range of -40°C to 100°C. POM's wear resistance and self-lubrication surpass most engineering plastics, and it also has good oil and peroxide resistance. By adding UV agents, its UV resistance can be significantly improved.

POM FW-715C is a specific grade of POM, natural in color and granular, suitable for injection molding. Its tensile strength at 23°C is 54 MPa, with a static friction coefficient of 0.09 and a dynamic friction coefficient of 0.11. POM FW-715C has an elongation of 35%, with high flexural modulus and flexural strength of 2900 MPa and 78 MPa, respectively. Regarding thermal deformation temperature, it is 160°C at 0.45 MPa and 125°C at 1.8 MPa in an unannealed state.

Additionally, POM FW-715C has low Taber wear and good cantilever beam notched impact performance, with values of 10 mg/1000 cycles and 6.12 kJ/m² at room temperature, respectively. Its specific gravity is 1.48 g/cm³, with a shrinkage rate of 1.7% in the flow direction and 2% in the vertical direction. The material has a Rockwell hardness of 70 and a fire rating of UL94 HB for thicknesses ranging from 0.95 to 2.9 mm, suitable for black, white, and red materials.

 

Mechanical behaviorConditionStandardValueUnit
Tensile StrengthBreak 23°CASTM D63854MPa
Friction CoefficientStaticASTM D37020.09 
Friction CoefficientDynamicASTM D37020.11 
Elongation23°CASTM D63835%
Tiber wear and tear ASTM D104410mg/1000cy
Flexural Modulus23°CASTM D7902900MPa
Flexural Strength23°CASTM D79078MPa
Izod Notch Impact ASTM D25656.12kJ/m²
Izod Notch Impact23°CASTM D2566.12kJ/m²
ThermalConditionStandardValueUnit
HDTUnannealed 0.45MPaASTM D648160°C
HDTUnannealed 1.8MPaASTM D648125°C
Physical propertyConditionStandardValueUnit
Density ASTM D7921.48g/cm³
ShrinkageFlowASTM D9951.7%
ShrinkagexFlowASTM D9952%
HardnessConditionStandardValueUnit
Rockwell HardnessM(Scale)ASTM D78570 
FlammabilityConditionStandardValueUnit
Flame RatingBlack, white, red 0.95-2.9mmUL94HB 

 