ABS PA-797 Plastic Pellets Properties Uses and Technical Data
Product Struction
What is ABS PA-797 Plastic Pellets?
ABS PA-797 is a high-strength, chemically resistant ABS plastic pellet designed for injection molding to meet the requirements of demanding applications. Its HB flame retardant properties make it an ideal material in the field of fire prevention, especially for environments with high requirements for fire resistance. With its excellent chemical resistance and mechanical properties, ABS PA-797 is widely used in many industries such as home appliances, kitchenware, communication equipment and bathroom products.
As an injection grade material, ABS PA-797 plastic pellet has excellent processing characteristics and is particularly suitable for complex injection molding processes. It maintains high dimensional stability during the molding process and ensures the production of precision components. The lubricant and release agent added to the material effectively improve the fluidity, promote the smooth progress of the molding process, while reducing the friction and time loss in the production process, and reduce the production cost.
The chemical resistance of ABS PA-797 plastic pellet enables it to resist the erosion of a variety of chemicals and maintain stable performance in long-term use. Whether used for home appliance housings, kitchen accessories, or functional parts for communication equipment and bathroom supplies, ABS PA-797 provides strong support and long-lasting durability. In addition, the HB flame retardant rating provides additional safety, allowing it to perform well in high temperatures and fire source environments.
Flammability | Condition | Standard | Value | Unit | |||
Flame | Rating All Color 1.5mm | UL94 | HB | ||||
Flame | Rating All Color 3.0mm | UL94 | HB | ||||
Mechanical behavior | Condition | Standard | Value | Unit | |||
Charpy | Notch Impact 23°C | ISO 179 | 35.5 | kJ/m² | |||
Elongation | 50mm/min | ISO 527 | 23 | % | |||
Flexural | Strength 2.0mm/min | ISO 178 | 51 | MPa | |||
Flexural | Modulus 2.0mm/min | ISO 178 | 1.1 | GPa | |||
Izod | Notch Impact 23°C | ISO 180 | 35 | kJ/m² | |||
Tensile | Strength Yield 50mm/min | ISO 527 | 43 | MPa | |||
Tensile | Strength Break 50mm/min | ISO 527 | 33 | MPa | |||
Physical property | Condition | Standard | Value | Unit | |||
Density | 23°C | ISO 1183 | 1.05 | g/cm³ | |||
Melt | Index 220°C 10kg | ISO 1133 | 9.2 | cm³/10min | |||
Shrinkage | ISO 294 | 0.4~0.7 | % | ||||
Thermal | Condition | Standard | Value | Unit | |||
CLE | ISO 11359 | 8.8E-5 | cm/cm/°C | ||||
HDT | Unannealed 1.8MPa | ISO 75 | 80 | °C | |||
HDT | Annealed 1.8MPa | ISO 75 | 99 | °C | |||
Vicat | Softening Temperature 50°C/hr 10N | ISO 306 | 105 | °C | |||
Vicat | Softening Temperature 50°C/hr 50N | ISO 306 | 95.5 | °C | |||
UL | Condition | Standard | Value | Unit | |||
Arc | Resistance | ASTM D495 | 6 | PLC | |||
Comparative | Tracking Index | IEC 60112 | 0 | PLC | |||
HAI | ALL 1.5mm | UL 746A | 0 | PLC | |||
HAI | ALL 3.0mm | UL 746A | 0 | PLC | |||
HVTR | UL 746A | 0 | PLC | ||||
HWI | ALL 1.5mm | UL 746A | 5 | PLC | |||
HWI | ALL 3.0mm | UL 746A | 4 | PLC | |||
RTI | Elec ALL 1.5mm | UL 746B | 60 | °C | |||
RTI | Elec ALL 3.0mm | UL 746B | 60 | °C | |||
RTI | Imp ALL 1.5mm | UL 746B | 60 | °C | |||
RTI | Imp ALL 3.0mm | UL 746B | 60 | °C | |||
RTI | Str ALL 1.5mm | UL 746B | 60 | °C | |||
RTI | Str ALL 3.0mm | UL 746B | 60 | °C | |||
UL | FlameRating ALL 1.5mm | UL94 | HB | ||||
UL | FlameRating ALL 3.0mm | UL94 | HB |
Click here to download TDS for ABS PA-797
【Related Recommendations】
ABS PA-709H:Tough, Low-Flow ABS Resin for Protective Equipment, Luggage Learn more>
ABS PA-765: High-Flow, UL94 V-0 ABS Resin for Automotive, Electronics Learn more>
ABS PA-756H:Flame-Retardant ABS with Fast Processing for Durable Learn more>