Overview of ABS D-90 Plastic Raw Material Pellets
Product Struction
ABS D-90 is a high gloss, strong rigid general purpose plastic particle, mainly suitable for injection molding process. ABS D-90 has been widely used in many industries due to its excellent mechanical properties and appearance.
1. Material characteristics
ABS D-90 has the characteristics of high gloss, high rigidity and excellent bending resistance, which can provide good impact resistance and stability. Its superior heat resistance and electrical insulation properties make it stable in the general working environment, suitable for products requiring high durability and beautiful appearance.
2. Application field
ABS D-90 is widely used in toys, home appliance buttons, lamp holders, clock housings, office supplies and other fields. It can meet the high requirements of durability, appearance and processing accuracy in product manufacturing, and is suitable for the production of various consumer and industrial products.
3. Processing method
ABS D-90 is mainly processed by injection molding process, which has the characteristics of high efficiency and precision, and can produce high-quality parts on a large scale. This process ensures dimensional stability and consistency for modern manufacturing needs.
| UL | Condition | Standard | Value | Unit |
| RTI | Elec All Color 1.5mm | UL 746B | 60 | °C |
| RTI | Elec All Color 3.0mm | UL 746B | 60 | °C |
| RTI | Imp All Color 1.5mm | UL 746B | 60 | °C |
| RTI | Imp All Color 3.0mm | UL 746B | 60 | °C |
| RTI | Str All Color 1.5mm | UL 746B | 60 | °C |
| RTI | Str All Color 3.0mm | UL 746B | 60 | °C |
| Flame Rating | All Color 1.5mm | UL94 | HB | |
| Flame Rating | All Color 3.0mm | UL94 | HB | |
| Mechanical behavior | Condition | Standard | Value | Unit |
| Elongation | 50mm/min | ISO 527 | 15 | % |
| Elongation | 6mm/min 3.2mm | ASTM D638 | 15 | % |
| Flexural Strength | 2.0mm/min | ISO 178 | 78 | MPa |
| Flexural Strength | 2.8mm/min 6.4mm | ASTM D790 | 790 | kg/cm² |
| Flexural Modulus | 2.0mm/min | ISO 178 | 2.3 | GPa |
| Flexural Modulus | 2.8mm/min 6.4mm | ASTM D790 | 26000 | kg/cm² |
| Izod Notch Impact | 23°C 4.0mm | ISO 180 | 14 | kJ/m² |
| Izod Notch Impact | 23°C 6.4mm | ASTM D256 | 16 | kg-cm/cm |
| Izod Notch Impact | 23°C 3.2mm | ASTM D256 | 17 | kg-cm/cm |
| Tensile Strength | 50mm/min | ISO 527 | 48 | MPa |
| Tensile Strength | 6mm/min 3.2mm | ASTM D638 | 480 | kg/cm² |
| Charpy Notch Impact | 23°C 4.0mm | ISO 179 | 15 | kJ/m² |
| Thermal | Condition | Standard | Value | Unit |
| HDT | Annealed 1.8MPa | ISO 75 | 95 | °C |
| HDT | Unannealed 1.8MPa | ISO 75 | 80 | °C |
| HDT | Annealing treatment at 85°C for 8 hours | ASTM D648 | 99 | °C |
| HDT | Unannealed | ASTM D648 | 88 | °C |
| Vicat Softening Temperature | 50°C/hr 10N | ISO 306 | 104 | °C |
| Vicat Softening Temperature | 50°C/hr 3.2mm | ASTM D1525 | 105 | °C |
| Physical property | Condition | Standard | Value | Unit |
| Density | 23°C | ISO 1183 | 1.04 | g/cm³ |
| Density | 23°C | ASTM D792 | 1.05 | g/cm³ |
| Melt Index | 200°C 5kg | ISO 1133 | 2.1 | cm³/10min |
| Melt Index | 220°C 10kg | ISO 1133 | 22 | cm³/10min |
| Melt Index | 200°C 5kg | ASTM D1238 | 2.1 | g/10min |
| Hardness | Condition | Standard | Value | Unit |
| Rockwell Hardness | R(Scale) | ASTM D785 | 105 | |
| Rockwell Hardness | R(Scale) 12.7mm | ASTM D785 | 110 | |
| Flammability | Condition | Standard | Value | Unit |
| Flame Rating | All Color 1.5mm | UL94 | HB | |
| Flame Rating | All Color 3.0mm | UL94 | HB |