BASF PSU 2010 | High Flowability PSU Polysulfone for Household
โครงสร้างผลิตภัณฑ์
What is PSU Polysulfone
Basf PSU 2010 is a flame-retardant grade PSU Polysulfone material, marked as PSU-FR, in granular form, suitable for injection molding process. This material features medium viscosity, flame retardancy, high-temperature resistance, dimensional stability and other characteristics. It has good fluidity. The unreinforced formula ensures stable processing performance even in complex mold designs. Its typical applications cover household items, automotive electronic connectors, electrical components and other fields with strict requirements for heat resistance and safety.
01 | Material Highlights and Characteristics
Flame retardant performance: Flame retardant grade HB - V2, which can meet the safety standards of various electrical and automotive applications.
Heat resistance performance: High heat resistance grade design, maintaining stable mechanical strength in long-term working environments.
Dimensional stability: Small deformation under high temperature and load conditions, ensuring the long-term reliability of components.
Processing adaptability: Medium-viscosity granules with excellent fluidity, suitable for injection molding of complex structural parts.
Non-reinforced formula: Maintains good toughness and molding flexibility, suitable for the requirements of lightweight and precision parts.
02 | PSU Polysulfone Basf Ultrason®S 2010 Data Sheet
คุณสมบัติทางไฟฟ้า | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
ซีทีไอ | มอก.60112 | 125 | วี | ||||
อิเล็กทริก | ความแข็งแกร่ง | ไออีซี 60243 | 40 | เควี/มม | |||
อิเล็กทริก | คงที่ 100Hz | มอก.60250 | 3.1 | ||||
อิเล็กทริก | คงที่ | มอก.60250 | 3.1 | ||||
การกระจายตัว | ปัจจัย 100Hz | มอก.60250 | 8 | ||||
การกระจายตัว | ปัจจัย 1MHz | มอก.60250 | 64 | ||||
พื้นผิว | ความต้านทาน | ไออีซี 60093 | 1E+15 | โอห์ม | |||
ปริมาณ | ความต้านทาน | ไออีซี 60093 | 1E+13 | Ω.ซม | |||
ความไวไฟ | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
เปลวไฟ | เรตติ้ง ทุกสี 0.75มม | UL94 | HB | ||||
เปลวไฟ | คะแนน ทุกสี 1.5มม | UL94 | HB | ||||
เปลวไฟ | เรตติ้ง ทุกสี 3.0มม | UL94 | วี-2 | ||||
ความแข็ง | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
ลูกบอล | Indentation Hardness | ISO2039 | 135 | MPa | |||
พฤติกรรมทางกล | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
ชาร์ปี | รอยบากกระแทก -30°C | ISO179 | 6 | กิโลจูล/ตรม | |||
ชาร์ปี | แรงกระแทก 23°C | ISO179 | 5.5 | กิโลจูล/ตรม | |||
ชาร์ปี | ผลกระทบที่ไม่เกิดรอยบาก -30°C | ISO179 | หมายเหตุ | กิโลจูล/ตรม | |||
ชาร์ปี | ผลกระทบที่ไม่เกิดรอยบาก 23°C | ISO179 | หมายเหตุ | กิโลจูล/ตรม | |||
การยืดตัว | ผลผลิต 23°C | ISO 527 | 6 | % | |||
ไอซอด | แรงกระแทก -30°C | ISO180 | 6 | กิโลจูล/ตรม | |||
ไอซอด | แรงกระแทก 23°C | ISO180 | 5.5 | กิโลจูล/ตรม | |||
แรงดึง | โมดูลัส 23°C | ISO 527 | 2550 | MPa | |||
แรงดึง | ความแข็งแรง ผลผลิต 23°C | ISO 527 | 75 | MPa | |||
คุณสมบัติทางกายภาพ | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
ความหนาแน่น | ISO1183 | 1.23 | กรัม/ซม.³ | ||||
ละลาย | ดัชนี 360°C 10กก. | ISO 1133 | 90 | cm³/10นาที | |||
การหดตัว | ไหล | ISO294 | 0.68 | % | |||
การหดตัว | xFlow | ISO294 | 0.72 | % | |||
น้ำ | การดูดซึม 50RH | ISO62 | 0.3 | % | |||
น้ำ | Absorption Saturation | ISO62 | 0.8 | % | |||
ความร้อน | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
คลี | ไหล | วิธีการภายใน | 5.3E-5 | ซม./ซม./°C | |||
เอชดีที | 1.8MPa | ISO75 | 176 | องศาเซลเซียส | |||
แอล | เงื่อนไข | มาตรฐาน | ค่า | หน่วย | |||
อาร์ค | ความต้านทาน | แอสทาม D495 | 6 | พีแอลซี | |||
การเปรียบเทียบ | ดัชนีการติดตาม | มอก.60112 | 3 | พีแอลซี | |||
อิเล็กทริก | ความแข็งแกร่ง | มาตรฐาน ASTM D149 | 50 | เควี/มม | |||
มิติ | ความเสถียร | ยูแอล 746 | 0.0 | % | |||
ฮ่าย | ทั้งหมด 0.75 มม. | มอก.746A | 1 | พีแอลซี | |||
ฮ่าย | ทั้งหมด 1.5 มม. | มอก.746A | 0 | พีแอลซี | |||
ฮ่าย | ทั้งหมด 3.0 มม. | มอก.746A | 0 | พีแอลซี | |||
เอชวีทีอาร์ | มอก.746A | 2 | พีแอลซี | ||||
เอช ดับบลิว ไอ | ทั้งหมด 0.75 มม. | มอก.746A | 3 | พีแอลซี | |||
เอช ดับบลิว ไอ | ทั้งหมด 1.5 มม. | มอก.746A | 3 | พีแอลซี | |||
เอช ดับบลิว ไอ | ทั้งหมด 3.0 มม. | มอก.746A | 2 | พีแอลซี | |||
สทท | สายไฟฟ้า ALL 0.75mm | UL 746B | 155 | องศาเซลเซียส | |||
สทท | อิมป์ออลล์ 0.75มม. | UL 746B | 130 | องศาเซลเซียส | |||
สทท | ลวดไฟฟ้าALL 1.5มม | UL 746B | 155 | องศาเซลเซียส | |||
สทท | อิมพีเรียลทั้งหมด 1.5 มม | UL 746B | 130 | องศาเซลเซียส | |||
สทท | สเตรออล 1.5มม | UL 746B | 155 | องศาเซลเซียส | |||
สทท | ไฟฟ้า ALL 3.0มม | UL 746B | 155 | องศาเซลเซียส | |||
สทท | อิมพ์ทั้งหมด 3.0มม | UL 746B | 130 | องศาเซลเซียส | |||
สทท | สเตรออล 3.0มม | UL 746B | 155 | องศาเซลเซียส | |||
แอล | ทนเปลวไฟได้ทั้งหมด 0.75 มม. | UL94 | HB | ||||
แอล | พิกัดเปลวไฟทั้งหมด 1.5 มม | UL94 | HB | ||||
แอล | พิกัดเปลวไฟทั้งหมด 3.0 มม | UL94 | วี-2 | ||||
ปริมาณ | ความต้านทาน | มาตรฐาน ASTM D257 | 1.0E15 | Ω.ซม |
03 | Technical Process Analysis
Basf PSU 2010 adopts injection molding process and is particularly suitable for high-precision and complex-structured products.
・Medium-viscosity particles: They have excellent melt fluidity during injection molding and can reduce the filling pressure.
・Mold compatibility: Good thermal stability can reduce dimensional shrinkage during the cooling process and enhance product consistency.
・Surface quality: The formed parts have a high degree of smoothness and are suitable for terminal applications with high requirements for appearance.
This makes Ultrason®S 2010 PSU Polysulfone perform well in small and complex structures such as automotive electronic connectors.
04 | Industry Application Scenarios
Household items: Excellent heat resistance and chemical resistance, suitable for kitchen and electrical components that need to be used for a long time.
Automotive electronics: Ensure the stability of electronic connectors and electrical components in the high-temperature engine compartment environment.
Electrical components: Flame retardancy and dimensional stability make it an ideal choice for insulators, housings and connectors.
05 | Market Trends and Customer Feedback
Recently, the demand for PSU Polysulfone in the fields of new energy vehicle electronics and smart home has been continuously increasing. Purchaser feedback: The triple advantages of "high heat resistance + flame retardancy + processing stability" of PSU 2010 have effectively solved:
-The pain point of plastic parts being prone to deformation in high-temperature environments
-The risk of electrical components not meeting the flame retardant grade standards
-The defect rate problem caused by insufficient fluidity in the injection molding process
06 | Procurement Process and FAQ
Q1: Is PSU 2010 suitable for high-temperature electrical environments?
A1: Yes, this material features high heat resistance and flame retardancy, making it suitable for long-term high-temperature working conditions.
Q2: Does this PSU Polysulfone material need additional reinforcement to be applied in automotive electronics?
A2: No need. The dimensional stability and fluidity of PSU 2010 have met the requirements of such applications.
Q3: How to ensure the stability of the supply chain?
A3: Through Juyuan's global channels, stable supply and rapid delivery support can be obtained.
Q4: What are the suitable processing methods?
A4: Injection molding is the main process, suitable for large-scale production of precision parts.
07 | Similar recommendation materials
ผู้ผลิต | Product Grade | ความหนาแน่น | Melt Flow Index | ความต้านแรงดึง | การยืดตัว | การหดตัว | อุณหภูมิการหลอมละลาย | โมดูลัสแรงดึง | อุณหภูมิการเบี่ยงเบนความร้อน | Notched Izod Impact | Linear Expansion Coefficient |
BASF | 2010 G4 | 1.38 g/cm³ | 40 cm³/10min | 115 MPa | 2.90% | 0.31% | - | 6600 MPa | 184 °C | 8.0 kJ/m² | 2.6E-5 cm/cm/°C |
BASF | 2010 G6 | 1.46 g/cm³ | 30 cm³/10min | 125 MPa | 2.20% | 0.29% | - | 8900 MPa | 185 °C | 8.5 กิโลจูล/ตรม. | 2E-5 cm/cm/°C |
BASF | 2010 NAT | 1.23 g/cm³ | 90 cm³/10min | 75 MPa | 6% | 0.68% | 330~390 °C | 2550 MPa | 176 °C | 5.5 กิโลจูล/ตรม. | 5.3E-5 cm/cm/°C |
BASF | 2010 G4 UN | 1.38 g/cm³ | 45 cm³/10min | 115 MPa | 2.90% | 0.31% | 350~390 °C | 6600 MPa | 184 °C | 8.5 กิโลจูล/ตรม. | 2.6E-5 cm/cm/°C |
BASF | 2010 G4 SW 15038 | 1.38 g/cm³ | 45 cm³/10min | 115 MPa | 2.50% | 0.31% | 350~390 °C | 6400 MPa | 184 °C | 8 kJ/m² | 2.6E-5 cm/cm/°C |
BASF | 2010 G6 UN | 1.46 g/cm³ | 30 cm³/10min | 125 MPa | 2.20% | 0.29% | 350~390 °C | 8900 MPa | 185 °C | 8.5 กิโลจูล/ตรม. | 2E-5 cm/cm/°C |
08 | The supply advantage of Juyuan
As a supplier with 24 years of international experience in plastic raw material trade, Juyuan is committed to providing customers with:
-Global direct procurement channels: Established stable cooperation with multiple international producers to ensure the authenticity of the goods and the continuity of supply.
-Customized services: Based on the customer's industry and application scenarios, provide selection suggestions and alternative solutions;
-Fast delivery: Relying on the international logistics network, shorten the procurement cycle and reduce the inventory pressure on customers;
-Technical support: Provide customers with process parameter references and application guidance to help enhance production stability.
【ข้อแนะนำที่เกี่ยวข้อง】
A Complete Guide to China’s Major Plastic Raw Material Procurement Hubs & Markets เรียนรู้เพิ่มเติม>
RTP PSU EMI 961 Polysulfone Plastic for EMI & ESD Protection เรียนรู้เพิ่มเติม>
Americhem PSU-GF30HF High-flow PSU Resin for Injection Molding เรียนรู้เพิ่มเติม>